Treatments enhancing appearance include such processes as napping and shearing, brushing, singeing, beetling, decating, tentering, calendering or pressing, moiréing, embossing, creping, glazing, polishing, and optical brightening.

Napping and shearing

Napping is a process that may be applied to woollens, cottons, spun silks, and spun rayons, including both woven and knitted types, to raise a velvety, soft surface. The process involves passing the fabric over revolving cylinders covered with fine wires that lift the short, loose fibres, usually from the weft yarns, to the surface, forming a nap. The process, which increases warmth, is frequently applied to woollens and worsteds and also to blankets.

Shearing cuts the raised nap to a uniform height and is used for the same purpose on pile fabrics. Shearing machines operate much like rotary lawn mowers, and the amount of shearing depends upon the desired height of the nap or pile, with such fabrics as gabardine receiving very close shearing. Shearing may also be applied to create stripes and other patterns by varying surface height.

Brushing

This process, applied to a wide variety of fabrics, is usually accomplished by bristle-covered rollers. The process is used to remove loose threads and short fibre ends from smooth-surfaced fabrics and is also used to raise a nap on knits and woven fabrics. Brushing is frequently applied to fabrics after shearing, removing the cut fibres that have fallen into the nap.

Singeing

Also called gassing, singeing is a process applied to both yarns and fabrics to produce an even surface by burning off projecting fibres, yarn ends, and fuzz. This is accomplished by passing the fibre or yarn over a gas flame or heated copper plates at a speed sufficient to burn away the protruding material without scorching or burning the yarn or fabric. Singeing is usually followed by passing the treated material over a wet surface to assure that any smoldering is halted.

Beetling

Beetling is a process applied to linen fabrics and to cotton fabrics made to resemble linen to produce a hard, flat surface with high lustre and also to make texture less porous. In this process, the fabric, dampened and wound around an iron cylinder, is passed through a machine in which it is pounded with heavy wooden mallets.

Decating

Decating is a process applied to woollens and worsteds, synthetic and blended fibre fabrics, and various types of knits. It involves the application of heat and pressure to set or develop lustre and softer hand and to even the set and grain of certain fabrics. When applied to double knits it imparts crisp hand and reduces shrinkage. In wet decating, which gives a subtle lustre, or bloom, fabric under tension is steamed by passing it over perforated cylinders.

Tentering, crabbing, and heat-setting

These are final processes applied to set the warp and weft of woven fabrics at right angles to each other, and to stretch and set the fabric to its final dimensions. Tentering stretches width under tension by the use of a tenter frame, consisting of chains fitted with pins or clips to hold the selvages of the fabric, and travelling on tracks. As the fabric passes through the heated chamber, creases and wrinkles are removed, the weave is straightened, and the fabric is dried to its final size. When the process is applied to wet wools it is called crabbing; when applied to synthetic fibres it is sometimes called heat-setting, a term also applied to the permanent setting of pleats, creases, and special surface effects.

Calendering

Calendering is a final process in which heat and pressure are applied to a fabric by passing it between heated rollers, imparting a flat, glossy, smooth surface. Lustre increases when the degree of heat and pressure is increased. Calendering is applied to fabrics in which a smooth, flat surface is desirable, such as most cottons, many linens and silks, and various synthetic fabrics. In such fabrics as velveteen, a flat surface is not desirable, and the cloth is steamed while in tension, without pressing. When applied to wool, the process is called pressing and employs heavy heated metal plates to steam and press the fabric. Calendering is not usually a permanent process. Moiréing, embossing, glazing and ciréing, and polishing are all variations of the calendering process. Moiré is a wavy or “watered” effect imparted by engraved rollers that press the design into the fabric. The process, applied to cotton, acetate, rayon, and some ribbed synthetic fabrics, is only permanent for acetates and resin-treated rayons. Embossing imparts a raised design that stands out from the background and is achieved by passing the fabric through heated rollers engraved with a design. Although embossing was formerly temporary, processes have now been developed to make this effect permanent.Glazing imparts a smooth, stiff, highly polished surface to such fabrics as chintz. It is achieved by applying such stiffeners as starch, glue, shellac, or resin to the fabric and then passing it through smooth, hot rollers that generate friction. Resins are now widely employed to impart permanent glaze. Ciré (from the French word for waxed) is a similar process applied to rayons and silks by the application of wax followed by hot calendering, producing a metallic high gloss. Ciré finishes can be achieved without a sizing substance in acetates, which are thermoplastic (e.g., can be softened by heat), by the application of heat.

Polishing, used to impart sheen to cottons without making them as stiff as glazed types, is usually achieved by mercerizing the fabric and then passing it through friction rollers.

Creping

A crepe effect may be achieved by finishing. In one method, which is not permanent, the cloth is passed, in the presence of steam, between hot rollers filled with indentations, producing waved and puckered areas. In the more permanent caustic soda method, a caustic soda paste is rolled onto the fabric in a patterned form, or a resist paste may be applied to areas to remain unpuckered, and the entire fabric is then immersed in caustic soda. The treated areas shrink, and the untreated areas pucker. If the pattern is applied in the form of stripes, the effect is called plissé; an allover design produces blister crepe.

Optical brightening

Optical brightening, or optical bleaches, are finishes giving the effect of great whiteness and brightness because of the way in which they reflect light. These compounds contain fluorescent colourless dyes, causing more blue light to be reflected. Changes in colour may occur as the fluorescent material loses energy, but new optical whiteners can be applied during the laundering process.

Finishes enhancing the feel and drape of fabrics involve the addition of sizing, weighting, fulling, and softening agents, which may be either temporary or permanent.

Sizing

Sizing, or dressing, agents are compounds that form a film around the yarn or individual fibres, increasing weight, crispness, and lustre. Sizing substances, including starches, gelatin, glue, casein, and clay, are frequently applied to cottons and are not permanent.

Weighting

Weighting, in the processing of silk, involves the application of metallic salts to add body and weight. The process is not permanent but can be repeated.

Fulling

Also called felting or milling, fulling is a process that increases the thickness and compactness of wool by subjecting it to moisture, heat, friction, and pressure until shrinkage of 10 to 25 percent is achieved. Shrinkage occurs in both the warp and weft, producing a smooth, tightly finished fabric that may be so compact that it resembles felt.

Softening

Making fabrics softer and sometimes also increasing absorbency involves the addition of such agents as dextrin, glycerin, sulfonated oils, sulfated tallow, and sulfated alcohols.

Finishes improving performance

The performance of fabrics in use has been greatly improved by the development of processes to control shrinkage, new resin finishes, and new heat-sensitive synthetic fibres.

Shrinkage control processes are applied by compressive shrinkage, resin treatment, or heat-setting. Compressive, or relaxation, shrinkage is applied to cotton and to certain cotton blends to reduce the stretching they experience during weaving and other processing. The fabric is dampened and dried in a relaxed state, eliminating tensions and distortions. The number of warp and weft yarns per square inch is increased, contributing greater durability, and fabrics treated by this method are usually smooth and have soft lustre. The process involves spraying the fabric with water and then pressing the fabric against a steam-heated cylinder covered with a thick blanket of woollen felt or rubber. The manufacturer is often required to specify the residual shrinkage, or percentage of shrinkage, that may still occur after the preshrinking process.

Rayons and rayon blends may be stabilized by the use of resins, which impregnate the fibre. Such fabrics may also be stabilized by employing acetals to produce cross-linking, a chemical reaction. Such synthetics as polyesters and nylons, which are heat sensitive, are usually permanently stabilized by heat-setting during finishing.

Shrinkage of wools is frequently controlled by treatment with chlorine, partially destroying the scales that occur on wool fibres and thus increasing resistance to the natural tendency of wool to felt. Other methods employ coating with resins that attach to the scales in order to discourage felting shrinkage.

Durable press

Durable press fabrics have such characteristics as shape retention, permanent pleating and creasing, permanently smooth seams, and the ability to shed wrinkles, and thus retain a fresh appearance without ironing. Such fabrics may be safely washed and dried by machine. These useful characteristics are imparted by a curing process. Depending upon composition and desired results, fabrics may be precured, a process in which a chemical resin is added, the fabric is dried and cured (baked), and heat is applied by pressing after garment construction; or fabrics may be postcured, a process in which resin is added, the fabric is dried, made into a garment, pressed, and then cured.

Wash-and-wear was an early durable press process employing chemical treatment and curing of fabrics; at least light ironing was required to restore appearance. Later, however, processes were developed that allowed such fabrics to regain smoothness after home machine washing at moderate temperature, followed by tumble drying.

Crease resistance

Crease, or wrinkle, resistance is frequently achieved by application of a synthetic resin, such as melamine or epoxy.

Soil release

Soil release finishes facilitate removal of waterborne and oil stains from fabrics such as polyester and cotton blends and fabrics treated for durable press, which usually show some resistance to stain removal by normal cleaning processes. Other finishes have been developed that give fabrics resistance to water and oil stains.

Anti static finishes

The accumulation of static electricity in such synthetic fibres as nylon, polyesters, and acrylics produces clinging, which may be reduced by application of permanent anti static agents during processing. Consumers can partially reduce static electricity by adding commercial fabric softeners during laundering.

Antibacterial and anti fungus finishes

Antibacterial finishes are germicides applied to fabrics to prevent odours produced by bacterial decomposition, such as perspiration odours, and also to reduce the possibility of infection by contact with contaminated textiles. Fabrics may also be treated with germicides to prevent mildew, a parasitic fungus that may grow on fabrics that are not thoroughly dried. Both mildew and rot, another form of decay, may also be controlled by treatment with resins.

Wool and silk are subject to attack by moths but may be made moth repellent by the application of appropriate chemicals either added in the dye bath or applied to the finished fabric.

Waterproofing and water repellence

Waterproofing is a process applied to such items as raincoats and umbrellas, closing the pores of the fabric by application of such substances as insoluble metallic compounds, paraffin, bituminous materials, and drying oils. Water-repellent finishes are surface finishes imparting some degree of resistance to water but are more comfortable to wear because the fabric pores remain open. Such finishes include wax and resin mixtures, aluminum salts, silicones, and fluorochemicals.

Flameproof, fireproof, and fire-resistant finishes

Flameproof fabrics are able to withstand exposure to flame or high temperature. This is achieved by application of various finishes, depending upon the fabric treated, that cause burning to stop as soon as the source of heat is removed. Fireproofing is achieved by the application of a finish that will cut off the oxygen supply around the flame. Fire-resistant finishes cause fabrics to resist the spread of flame.

Reference: https://www.britannica.com/topic/textile/Moth-repellent-treatments